Rust bluing solution. Rust Bluing

To the helpful gentleman that recommended the use of reagent-grade materials, you can obtain these materials from www. All blued parts still require oiling to prevent rust. To initiate and accelerate the rusting process. It'll actually be cheaper, even with gas as it is. Then an acid solution is applied to the metal, the acid will accelerate the rusting. My local chem supply has everything I need but the acids come in different strengths. I tried a cold bluing formula developed at the turn of the century that is, the formerbut it was a poor result, because I used one that was based on a copper nitrate [affil.

 

Rust blue is the authentic black iron oxide finish used by professional gun makers. star · Research. Proven formulas that can accurately reproduce the correct.Bluing is often a hobbyist endeavor, and there are many methods of bluing, and continuing debates about the relative efficacy of each method.

 

Modern home hobbyist versions of this process typically use a hydrogen peroxide and salt solution, sometimes with vinegar, for the rusting.Privacy Email : [email protected].

 

Baking soda or just real soap for an alkaline water to cook in should do the trick! Modern detergents are neutral; any kind of soda (crystal soda, baking soda.If you let it go too long, it will pit the metal.

 

Rust bluing for barrels and magazine tubes is a process that only a few master gunsmiths practice. Coating the clean parts with a rust bluing solution.I have also used staples and steel wool.

 

Peroxide, iodized salt, a few drops of distilled water. degrease a half a pad of steel wool and dissolve it into the solution. Apply solution.Boil it, don't get greedy.

 

To make a homemade rust bluing solution, you will need access to zinc or manganese dihydrogan phosphate, water, a tank and an oxidizing agent, such as nitrate.Simply [

 

From rimfirecentral.

 

Decant this liquor into brown chemical bottles making sure that none of the sludge is carried into the bottles.

 

I think more acid vinegar might be needed to get the process to work better.

 

If you let it go too long, it will pit the metal.

 

I use the old military LSA

 

Professional Gunsmithing.

 

It's still got some thin spots that you've got to look closely to see in direct sunlight but I figure with a few more applications it will look as good as my M91 Carcano.

 

A solution of hydrochloric and nitric acids diluted in distilled water with a small quantity of iron filings added is prepared.

 

This formula does not require neutralization to prevent after-rusting.

 

ISBN

 

Thank you!

 

It may take several days.

 

Modified formula omitting mercury salts as a component.

 

Unknown December 15, at AM.

 

Testimonials What people think of Rust Blue

 

All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer.

 

It, too, must be oiled to provide any significant rust resistance.

 

From tfrecipes.

 

Great product.

 

It is named after the blue-black appearance of the resulting protective finish.

 

The parts must be observed constantly for colour change.

 

I have read a lot on rust blueing, and done a few guns.

 

I use a solution very similar to John Gellatly's, only I use powdered iron not nails.Forum Rust bluing solution

 

I use the following formula, cc's pure Nitric Acid, cc's Hydrochloric acid [ Muriatic Acid [affil.

 

Fifth, if modern oils that contain synthetics or silicones have been on the surfaces you will have to clean them more than one time.

 

As you see, I am still pursuing the elusive blue.

 

Are there instructions for rust Browning and bluing?

 

And good luck - it'll be some of the most satisfying gun work you'll ever do!

 

The rusting always seems to cause a satin finish.

 

Featured Products Authentic Products … From rustblue.

 

Bluing, being a chemical conversion coating, is not as robust against wear and corrosion resistance as plated coatings, and is typically no thicker than 2.

 

forum? Round after round less rust will form.